Alloy Seamless Hastelloy Pipe UNS N06002 AMS 5587 AMS 5588 ASTM B619 ASTM B622

Heat Resistant (UNS N06002)
A wrought nickel base alloy with excellent high temperature strength and oxidation resistance. All of the product forms are excellent in terms of forming and welding. Although this alloy is primarily noted for heat and oxidation resistance it also has good resistance to chloride stress-corrosion cracking and has good resistance to carburization, excellent resistance to reducing or carburizing atmospheres. Alloy X is one of the most widely used nickel base superalloys for gas turbine engine components.

AMS 5754 has no yield or tensile strength requirements, but it does require a hardness maximum and stress rupture minimums. Strong and Oxidation Resistant to 2200 Deg. F (1200 Deg. C) - HASTELLOY alloy X is a solid solution strengthened grade has good strength and oxidation resistance up to 2200 Deg. F (1200 Deg. C).

Characteristics

RESISTANCE TO OXIDATION
The outstanding oxidation resistance of HASTELLOY alloy X is illustrated below. Tests were conducted by exposing samples to dry air at 2000 Deg. F. and to dry air pressurized to 300 psi at 1750 Deg. F. Two criteria for evaluating oxidation resistance are weight change and depth of corrosion penetration. HASTELLOY alloy X excels in both respects due to the formation of a protective, tenacious oxide film.

RESISTANCE TO CARBURIZATION AND NITRIDING
HASTELLOY alloy X also resists carburization and nitriding, two common conditions which often lead to early failure in high-temperature alloys. After 100 hours in petroleum coke, four other materials were completely penetrated by carburization; whereas, Alloy X specimens showed no carburization at all. Of ten materials evaluated in an atmosphere of hydrogen, nitrogen and ammonia at 1100 Deg. F. and 25,00 psi for 64 days, Alloy X had a nitride case less than one-fourth as thick as the closest competitive material without intergranular attack.

Applications

The alloy finds use in petrochemical process equipment and gas turbines in the hot combustor zone sections. Also used for structural components in industrial furnace applications because of the excellent oxidation resistance.

HASTELLOY alloy X is recommended especially for use in furnace applications because it has unusual resistance to oxidizing, reducing, and neutral atmospheres. Furnace rolls made of this alloy were still in good condition after operating for 8700 hours at 2150 Deg. F. Furnace trays, used to support heavy loads, have been exposed to temperatures up to 2300 Deg. F. in an oxidizing atmosphere without bending or warping. Alloy X is equally suitable for use in jet engine tailpipes, afterburner components, turbine blades, nozzle vanes, cabin heaters, and other aircraft parts.

Gas turbine combustion cans and ducting, heat-treating equipment.

Alloy X has wide use in gas turbine engines for combustion zone components such as transition duct, combustor cans, spray bars and flame holders as well as in afterburners, tailpipes and cabin heaters. It is recommended for use in industrial furnace applications because it has unusual resistance to oxidizing, reducing and neutral atmospheres. Furnace rolls of this alloy were still in good condition after operating for 8,700 hours at 2150 degrees F (1177 degrees C). HASTELLOY alloy X is also used in the chemical process industry for retorts, muffles, catalyst support grids, furnace baffles, tubing for pyrolysis operations and flash drier components.

Useful Properties for Aircraft and Furnace Parts - HASTELLOY alloy X is recommended especially for use in furnace applications because it has unusual resistance to oxidizing, reducing, and neutral atmospheres. Furnace rolls made of this alloy were still in good condition after operation for 8,700 hours at 2150 Deg. F (1177 Deg. C).

Chemistry

Tensile Data

Specifications

Machinability RATING: 27% of B-1112

TYPICAL STOCK REMOVAL RATE: 45 surface feet/minute with high speed tools, 125 surface feet/minute with carbide.

COMMENTS:
Care must be taken to make sure there are rigid machine setup and sharp tools, so that work hardening and surface glazing do not occur. HASTELLOY alloy X is machinable in both the wrought and cast form. Low cutting speeds and an ample flow of coolant are required.

Suggested tool angles for single point tungsten carbide tools are 8- to 10-Deg. side-rake angle from cutting edge, 5- to 8-Deg. back-rake angle, 5- to 7-Deg. end relief angle, and 15- to 30-Deg. side cutting-edge angle. Nose radius should be 1/32 to 1/16 inch.

High-speed steel drills should be ground to an included angle of 135 to 140 Deg. with a clearance angle of 10 degrees. The web should be thinned down to about one-third the web-thickness of a standard drill.

Better finishes can be obtained by increasing the speed and decreasing the feed. Automatic screw machines are not recommended because speeds are generally excessive and carbide-tipped tools will not hold up. A sulfur-base cutting fluid should be used for machining this alloy. All traces of cutting fluid should be removed prior to heat-treatment or high temperature service.

The following table may be used as a guide in machining HASTELLOY alloy X. The figures will be modified by such factors as tool size and type, type of machining equipment, size of stock, and nature of cut.

Heat-Treatment

All wrought forms of HASTELLOY alloy X are furnished in the solution heat-treated condition unless otherwise specified. The standard heat-treatment is at a temperature of 2150 Deg. F (1177 Deg. C) followed by rapid cooling. Other heat-treatment temperatures also may be effective for certain forms and conditions.

The properties listed here are average values based on laboratory test conducted by the manufacturer. They are indicative only of the results obtained in such tests and should not be considered as guaranteed maximums or minimums. Materials must be tested under actual service conditions to determine their suitability for a particular purpose. All data represent the average of six or less tests unless otherwise noted. All data shown for material aged for 1,000, 4,000, 8,000, and/or 16,000 hours are based on tests of a single heat. The secondary units (metric) used in this booklet are those of the SI system.

Product : Butt-Welding Fitting Material: SA234,SA403 Grade: Materials: •Carbon steel: ASTM A234, WPB, WPC, ASTM A420 WPL1, WPL3, WPL6, WPHY-42/ 46/52/56/60/65/70 Stainless steel: ASTM A403 WP304/304L, WP316/316/L, WP321, WP347 and WPS31254 Alloy steel: ASTM A234 WP1/WP12/WP11/WP22/WP5/WP7/WP9/WP91 Duplex and super duplex steel: ASTM A815 UNS S31803/S32750/S32760 Special alloy steel: Monel400 and Inconel 600/800/825/C276 Executive Standard: ASME B 16.9, GB/T12459, DIN, JIS, BS, etc Product Type: Elbow(Long,Short),Return(Long,Short),Tee,Cross,Cap, Reducer…etc. Size(NPS): Long Radius Elbow,Straight Tee and Cross,Cap (1/2” to 48”). Short Radius 180 deg Return,Short Radius Elbow(1” to 24”). Long Radius Return (1/2” to 24”). Long Radius Reducing Elbow (2” x 1-1/2” to 24” x 12”). Reducing Outlet Tee and Reducing Outlet Cross (1/2” x 1/2” x 3/8” to 48” x 48” x 22” ). Reducer (3/4” x 1/2” to 48” x 40” ). Flange Type WN/welding neck flange;SO/slip on flange; PL /Plate flange;BL/Blind flange; Th/Threaded flange;SW/socket welding flange; LF/SE(lapped flange/stub end);LWN/long welding neck flange; Orifice flange;Reducing flange;API flange; Integral/Compact flange;Spectacle blind, Line spade and spacer,Paddle blind,Paddle spacer; Orifice plate;Pipe plate,Bleed ring;Plate flange Standard ANSI B16.5,ANSI B16.47,ANSI B16.48,ANSI B16.36, JIS B2220, BS4504, BS1560,BS10; MSS SP44 DIN2630,DIN2631,DIN2632,DIN2633,DIN2634,DIN2635, DIN2636,DIN2637,DIN2638,DIN2501(WN);DN2573,DIN2576, DIN2527,DIN2655,DIN2656(PL);DIN2566(TH) Size 1/2''~60'' Class Rating 150~2500 Facing RF(raised face);FF(flat face);RTJ(ring type joint);RJ(ring joint face) TG(tongue and groove face);MFM(male and female face) Manufacturing process Push, Press, Forge, Cast, etc. Material Carbon steel Stainless steel Alloy steel Duplex stainless steel Carbon steel, stainless steel, alloy steel ASTM A694 F42,F46,F48,F50,F52,F56,F60,F65,F70; ASTM A234 WPB,WPC; ASTM A420 WPL6,WPL3; ASTM A105; ASTM A860; ASTM A350 LF1, LF2 CL1/CL2, LF3 CL1/CL2; ASTM A266 GR.1,GR.2,GR.3,GR.4 API 5L GR.B ASTM A182 F 304, 304L, 304H, 309S, 309H, 310S, 310H,316, 316Ti,316L,317, 317L, 321, 347,347H,348,254SMO, S31254,UNS 8020,F45,S30815,F46,S30600,F904L A182 F56,S33228,F58,S31266,F62,N08367, ASTM A312 ASTM A182 F5, F5a , F9, F11, F12, F22, F91; ASTM A182 F51/UNS S31803,F53/UNS S32750,F55/UNS S32760 Packing Wooden cases, pallets, nylon bags or according to the customers' requirements MOQ 1pcs Delivery time 10-100 days depending on quantity Payment terms T/T Shipment FOB Shanghai, CFR, CIF etc Application Petroleum/Power/Chemical/Construction/Gas/Metallurgy/Shipbuilding etc Remarks Other materials and drawings are available. Products Flanges WN(welding-neck);SO(slip-on);PL(Plate);BL(Blind);TH (Threaded);SW(socket-welding);LF/SE(lapped flange/stub end);LWN(long welding neck);Orifice flange; Reducing flange; API flange; Integral/Compact flange; Spectacle blind ,Lind spade and spacer, Paddle blind, Paddle spacer ; Orifice plate; Pipe plate ,Bleed ring. standard American standard ANSIB16.5,B16.7,/API605,6A,6B/MSS SP44/AWWA C207 German standard DIN2630,2631,2632,2633,2634,2635,2636,2637,2638, 2501 (WN); DIN2573,2576,2527,2655,2656(PL);DIN2566 (TH) British Standard BS4504 PN16,PN40/BS10 Japan Standard JIS/KS5K,10K ,16K, 20K Russia Standard GOST12820,12821 Chinese Standard Non- standard According to drawing size from 10mm-5000mm, weight from 0.5K to30 tons Size 1/2”-60” Material Carbon Steel ASTM A106 GR.B, GR.C,;ASTM A333 GR.1, GR.3, GR.6; ASTM/ ASME S/A179/ A 179M; ASTM/ ASME S/A192/ A 192M; ASTM/ ASME S/A210/ A 210M GR.A;API 5L GR.B, X42, X52, X60, X65; ASTM A860/ A 860M WPHY42, WPHY52, WPHY60, WPHY65, WPHY70; ASTM A694 / A 694M F42, F46,F48,F50,F52,F56, F60, F65, F70; ASTM/ ASME S/A234/ A 234M WPB,WPC; ASTM/ ASME S/A420/ A 420M WPL6, WPL3; ASTM/ ASME S/A105/ A 105M; ASTM/ ASME S/A266/ A 266M GR.1, GR.2, GR.3, GR.4; ASTM/ ASME S/A350/ A 350M LF1, LF2,LF3; ASTM A193 B7, A307 B, A 320 L 7;; Alloy Steel ASTM/ASMES/A335/A315MP5,P9,P11, P12,P22,P91; ASTM/ASMES/A213A 213MT5,T9,T11, T12,T22,T23T91; DIN1717510CrMo910,13CrMo44, 10Cr9Mo1VNb;WB36(15NiCuMoNb5); ASTM/ASMES/A234/A234MWP5,WP9, WP11,WP12,WP22, WP9; ASTM/ASMES/A182/A182MF5,F5a , F9,F11,F12,F22, F91; ASTM/ ASME S/A336/ A 336M F5, F9, F11, F12, F22, F91. Stainless Steel ASTM/ASMEA/SA182F304,304L, 304H,309S,309H,310S,310H, 316,316TI,16H,316L,316LN,317,317L, 321,321H,347,347H,348,348H, F40/S31254,F20/N08020,F45/S30815, F46/S30600,F47/S31725,F48/S31726, F49/S34565,F56/S33228,F58/S31266, F62/N08367/1.4529 Duplex Steel/Super Duplex Steel ASTM/ASMEA/SA182F51/2205/S31803/1.4462 ; F53/2507/S32750/1.4410; F55/S32760,F50/S31200;F57/S39277; F59/S32520;F60/S32205; F61/S3225F904L/N08904/1.4539; 254SMO/S31254/1.4574;S31050/1.4466; 17-4PH/S1400/1.4548724L;316Lmod/1.4435; 725LN/310MoLN UNS S31254/254SMo/F44,S31200/F50,S31803 /F51/SAF2205, S32950/F52,S32750/F53/SAF2507, S39274/F54,S32760/F55,S39277/F57,S32520/F59, S32205/F60,F62/No8367,S32550/F61/00cr25ni6. 5mo3cun,S32906/F65 TOBO GROUP Eddy current test Direct-reading spectrometer Ultrasonic detector hydraulic test equipment Chemistry laboratory Universal testing machine Universal testing machine Hardness tester Metallography microscope imported Micro-analysis Chemical analysis Always seeking for perfection is our survival base. Modern enterprise pursues"Human-centered concept". We start with improving the quality of staff, and try to let us exert potential ability, so as to reach quality awareness, ensure first class quality. Perfection, is the persistent to details, perfection, is the challenge to technology, perfection, is the understanding to the foreword, perfection, is the nitpick to quality, perfection, is the fanaticism to highest level. Wire cutting machine Arldirect-reading spectrometer Impact tester equipment