The tensile properties of the pipe fitting materials shall comply with the tensile properties requirements. Tests and reports shall be conducted in accordance with A370 methods and definitions.
For tensile testing, longitudinal or transverse cut specimens should be acceptable. Although tensile properties Table specifies the elongation requirements for the longitudinal and transverse specimens, it is not intended to be applicable at the same time. Instead, This intent that only the corresponding elongation requirements for specimens that are applicable in the direction are appropriate.
Tensile Properties
The tensile properties of the pipe fitting materials shall comply with the tensile properties requirements. Tests and reports shall be conducted in accordance with A370 methods and definitions.
For tensile testing, longitudinal or transverse cut specimens should be acceptable. Although tensile properties Table specifies the elongation requirements for the longitudinal and transverse specimens, it is not intended to be applicable at the same time. Instead, This intent that only the corresponding elongation requirements for specimens that are applicable in the direction are appropriate.
Tensile Properties
The tensile properties of the pipe fitting materials shall comply with the tensile properties requirements. Tests and reports shall be conducted in accordance with A370 methods and definitions.
For tensile testing, longitudinal or transverse cut specimens should be acceptable. Although tensile properties Table specifies the elongation requirements for the longitudinal and transverse specimens, it is not intended to be applicable at the same time. Instead, This intent that only the corresponding elongation requirements for specimens that are applicable in the direction are appropriate.
Tensile test report made on the starting material shall notes:
• The starting material report shall demonstrate that the properties of the pipe fittings material meet the requirements of this standard, provided that the heat treatment of the initial material is the same as that of the pipe fittings material.
• If the initial material has not been tested, or if the heat treatment of the initial material is different from that of the pipe fittings, the fitting manufacturer shall conduct at least one tensile test per furnace steel on the material representing of the finished pipe fittings, and the heat treatment condition shall be the same as that of the pipe fittings represented.
Chemical Composition
The chemical composition of each cast or furnace steel shall be determined and shall comply with the chemical composition requirements for each grade of material listed in the chemical composition table.
Chemical Composition (%) of ASTM A403
| Steel No. | Type | Chemical composition |
| C | Si | S | P | Mn | Cr | Ni | Mo | Other | ób | ós | δ5 |
| WP304 | 0.08 | 1 | 0.03 | 0.045 | 2 | 18-20 | 8-11 | | | 515 | 205 | 28 | |
| WP304H | 0.04-0.1 | 1 | 0.03 | 0.045 | 2 | 18-20 | 8-11 | | | 515 | 205 | 28 | |
| WP304L | 0.035 | 1 | 0.03 | 0.045 | 2 | 18-20 | 8-13 | | | 485 | 170 | 28 | |
| WP304LN | 0.03 | 0.75 | 0.03 | 0.045 | 2 | 18-20 | 8-10.5 | | N2:0.1-0.16 | 515 | 205 | 28 | |
| WP304N | 0.08 | 0.75 | 0.03 | 0.045 | 2 | 18-20 | 8-11 | | N2:0.1-0.16 | 550 | 240 | 28 | |
| WP309 | 0.15 | 1 | 0.03 | 0.045 | 2 | 22-24 | 12-15 | | | 515 | 205 | 28 | |
| WP310 | 0.15 | 1.5 | 0.03 | 0.045 | 2 | 24-26 | 19-22 | | | 515 | 205 | 28 | |
| WP316 | 0.08 | 1 | 0.03 | 0.045 | 2 | 16-18 | 10-14 | 2-3 | | 515 | 205 | 28 | |
| WP316H | 0.04-0.1 | 1 | 0.03 | 0.045 | 2 | 16-18 | 10-14 | 2-3 | | 515 | 205 | 28 | |
| WP316LN | 0.03 | 0.75 | 0.03 | 0.045 | 2 | 16-18 | 11-14 | 2-3 | N2:0.1-0.16 | 515 | 205 | 28 | |
| WP316L | 0.035 | 1 | 0.03 | 0.045 | 2 | 16-18 | 10-16 | 2-3 | | 485 | 170 | 28 | |
| WP316N | 0.08 | 0.75 | 0.03 | 0.045 | 2 | 16-18 | 11-14 | 2-3 | N2:0.1-0.16 | 550 | 240 | 28 | |
| WP317 | 0.08 | 1 | 0.03 | 0.045 | 2 | 18-20 | 11-15 | 3-4 | | 515 | 205 | 28 | |
| WP317L | 0.03 | 1 | 0.03 | 0.045 | 2 | 18-20 | 11-15 | 3-4 | | 515 | 205 | 28 | |
| WP321 | 0.08 | 1 | 0.03 | 0.045 | 2 | 17-20 | 9-13 | | Ti:5C-0.7 | 515 | 205 | 28 | |
| WP321H | 0.04-0.1 | 1 | 0.03 | 0.045 | 2 | 17-20 | 9-13 | | Ti:4C-0.7 | 515 | 205 | 28 | |
| WP347 | 0.08 | 1 | 0.03 | 0.045 | 2 | 17-20 | 9-13 | | Nb+Ta:10C-1.1 | 515 | 205 | 28 | |
| WP347H | 0.04-0.1 | 1 | 0.03 | 0.045 | 2 | 17-20 | 9-13 | | Nb+Ta:8C-1 | 515 | 205 | 28 | |
| WP348 | 0.08 | 1 | 0.03 | 0.045 | 2 | 17-20 | 9-13 | | Ta:0.1 | 515 | 205 | 28 | |
| WP348H | 0.04-0.1 | 1 | 0.03 | 0.045 | 2 | 17-20 | 9-13 | | Ta:0.1 | 515 | 205 | 28 | |
Notes:
- For each reduction of 0.01% below the specified C maximum, an increase of 0.06% Mn above the specified maximum will be permitted, up to a maximum of 1.35%.
- The sum of Cu, Ni, Cr, and Mo shall not exceed 1.00%.
- The sum of Cr and Mo shall not exceed 0.32%.
- The maximum carbon equivalent (C.E.) shall be 0.50, based on heat analysis and the formula C.E.=C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15.
Material Furnished to this specification shall conform to the requirements of specifications A960/A960M including any supplementary requirements that are indicates in the purchase order . Failure to company with the common requirements of Specification A960/A960M constitutes non-conformance with this specification . In case of conflict between this specification and Specification A960/A960M , this specification shall prevail .